1) Carbon foam
碳凝胶
2) carbon aerogel
碳气凝胶
1.
The microstructure of carbon aerogel was investigated by using electron scanning microscope(SEM),pore size distribution and electrical conductivity measurement.
探索新型纳米多孔材料碳气凝胶的微结构控制,研究常压条件下纤维增强型碳气凝胶的制备,以及催化剂浓度、质量分数、纤维表面特性、溶胶注入纤维前的老化时间等制备参数对其微结构的影响。
2.
This paper examins carbon aerogel by SEM, BET and cyclic voltammetry.
在常压条件下通过溶胶-凝胶法和碳化、活化工艺制备碳气凝胶材料。
3.
The micro structure of the porous carbon aerogels is measured by SEM and BET.
经高温碳化处理 ,将RF有机气凝胶转化为碳气凝胶 ,改变RC比和聚合单体的质量百分数 ,可控制气凝胶的粒径及孔径、密度及比表面积。
3) carbon aerogels
碳气凝胶
1.
For the first time,hydroquinone-formaldehyde aerogels have been prepared by sol-gel method and CO_2 supercritical drying,and after high temperature carbonization the carbonized carbon aerogels are obtained.
首次用溶胶-凝胶法和CO2超临界干燥技术制备了对苯二酚-甲醛有机气凝胶,并经高温碳化处理得到其碳气凝胶,测得气凝胶的比表面积由碳化前的375。
2.
In this paper, carbon aerogels are obtained through ordinary pressure drying; their structural properties are investigated.
碳气凝胶是一种新型多孔碳材料,具有比表面积大、电导率高的特点。
3.
SEM, BET and pore size distribution techniques were used to characterize the morphology and pore structure of the carbon aerogels.
研究了碳气凝胶在常压条件下的制备过程和干燥方法。
4) carbon-silica gel
碳硅凝胶
1.
Meso-tetrakis(4-aminophenyl)porphyrin[T(4-TAP)P] used as a suitable chelating reagent was loaded on the mixture of active carbon-silica gel.
首次以meso-四(4-氨基苯基)卟啉为衍生化试剂,使其负载于碳硅凝胶填充材料上,在优化的实验条件下,于pH9。
5) Carbon Xerogel
碳干凝胶
1.
First, Pt embedded carbon xerogel catalysts are prepared by sol-gel method.
首先,利用Pt直接嵌入溶胶-凝胶法制备可调变粒径和孔结构的低Pt载量Pt/碳干凝胶(CX)催化剂。
6) gel pre-carbonization
凝胶预碳化
1.
6Bi4Ti4O15) nanocrystalline powder with small particle size and good dispersion was prepared via the gel pre-carbonization sol-gel method.
用凝胶预碳化处理工艺的溶胶-凝胶法制备了晶粒粒径小且分散性能较好的钙锶铋钛(Ca0。
补充资料：Sds-聚丙烯酰胺凝胶电泳凝胶电泳
sds-聚丙烯酰胺凝胶电泳（sds-page，sodium dodecyl sulfate-polyacrylamide gel electrohoresis）
在有去污剂十二烷基硫酸钠存在下的聚丙烯酰胺凝胶电泳。sds-page只是按照分子大小分离的，而不是根据分子所带的电荷和大小分离的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条