1) tin nickel alloy electroplate
Ni-Sn合金镀层
2) deposit of Ni-Sn-Cu-P alloy
Ni-Sn-Cu-P合金镀层
3) Sn-Ni alloy
Sn-Ni合金
1.
By introducing amino acid additives in the pyrophosphate plating bath,the Sn-Ni alloy coating containing 67% Sn(mass fraction),having similar color to Ni coating and excellent corrosion resistance as well,was prepared using electro-deposition.
采用氨基酸类添加剂在焦磷酸盐体系中电沉积出锡含量67%、颜色与镍镀层相仿、耐腐蚀性能优异的Sn-Ni合金镀层。
2.
The effect of process parameters such as current density,time,temperature,pH value,mixing method on the electric resistance and wear resistance of the gun colour Sn-Ni alloy coating were studied by orthogonal test,and the optimum process parameters were determined as follows: current density,0.
利用正交试验方法研究了电流密度、时间、温度、pH、搅拌方式等工艺参数对Sn-Ni合金枪黑色镀层电阻及耐磨性能的影响,确定了较优的工艺条件:Jκ=0。
3.
An ab initio method with the first-principles plane-wave pseudopotentials based on the density functional theory has been used to calculate the physical character and electrochemical performance of various alloy phases in Sn-Ni alloy.
采用基于密度泛函理论的第一性原理平面波赝势方法计算了Sn-Ni合金中2种稳定相结构的物理性质和电化学性质。
4) Ni-Sn alloy
Ni-Sn合金
1.
The characteristics and catalytic ability for hydrogen evolution reaction of Ni-Sn alloys prepared by electroplating
电沉积制备Ni-Sn合金电极材料的结构与电化学性能
5) Sn-Pb alloy electroplating
电镀Sn-Pb合金镀层
6) Ni-W alloy coatings
Ni-W合金镀层
1.
The effect of Tungsten on the microstructure of Ni-W alloy coatings prepared by the pulse electrodeposition technology is firstly investigated by X-ray Diffraction.
利用脉冲电沉积的方法制备了Ni-W合金镀层,在微观形貌上与用直流电沉积方法得到的镀层进行比较。
2.
Ni-W alloy coatings are prepared by pulse electrodeposition.
利用脉冲电沉积方法制备了Ni-W合金镀层,观察了该镀层在不同载荷下的摩擦磨损行为,探讨了该合金镀层的摩擦磨损机理,并与45钢进行了对比试验。
3.
Ni-W alloy coatings with excellent hardness, wear resistance and appearance produced by electrodeposition were introduced in this dissertation.
本文用电沉积方法制备了具有良好硬度、耐磨性和外观质量的Ni-W合金镀层。
补充资料：Ni3Al基金属间化合物高温合金
Ni3Al基金属间化合物高温合金
Ni_(3)Al-base intermetallic compound superalloy
N一3AIJ一J旧shuJ一an huahewu goowen heJ一nNi3AI基金属间化合物高温合金(Ni3AI一baseintermetallie eompound superalloy)以Ni3AI相为基体的金属间化合物高温合金。Ni3AI作为高温合金材料中的强化相口)早已被人们所熟知。单晶Ni3AI有较好的室温塑性和加工性，但多晶Ni3AI在室温的塑性儿乎为零。1979年，日本和泉修等发现，添加微量硼可使Ni3AI韧化。硼强烈地偏聚于晶界，从而提高晶界的结合强度并使晶界区无序化，因此提高了晶界区塑性变形能力，使Ni3AI的室温拉伸伸长率可达50%以上。纯净N珠AI的室温、高温强度偏低，与高温合金相比需要进一步提高。固溶强化(见高温合金固溶强化)是提高强度的一条有效途径。Ni3AI可以固溶很多元素，其中以错和铅的强化效果最显著。美国橡树岭国家试验室已发展了一系列含铬、错、错等元素的Ni3AI基金属间化合物高温合金，具有良好的强度、塑性和高温抗氧化性。中国也对Ni3AI基合金进行了深入研究，并添加微量镁显著改善了热加工塑性。Ni3AI基合金可能是最先在工业上得到使用的金属间化合物高温合金之一，已制成各种部件在试用，如汽轮机和柴油机的耐热部件、高温模具、加热元件以及航空用的紧固件等。 〔邹敦叙)