1) the material equivalent rigidity
材料等效弯曲模量
2) flexural modulus
弯曲模量
1.
Preparation and flexural modulus of biodegradable composites reinforced with kenaf fibers;
洋麻纤维增强全降解复合材料的制备及其弯曲模量
2.
Biodegradable composites reinforced with bagasse fibre were prepared by a press forming,and the thermal properties of fibre and the flexural modulus of composites were investigated in view of the fibre content and length.
利用压制成型制备了甘蔗渣纤维增强可降解复合材料,分析了纤维的热分解性能,研究了纤维含有量和纤维长度对材料弯曲模量的影响,利用Cox剪滞法和材料的结构特点,探讨了一种新的修正模型对弯曲模量的预测。
3.
The flexural strength and flexural modulus will reach the maximum value of 130 MPa and 4.
分别研究了丙烯腈基短切碳纤维含量、引发剂(过氧化苯甲酰,BPO)用量和HA的质量分数对复合材料弯曲强度和弯曲模量的影响。
3) Bending Modulus
弯曲模量
1.
In order to develop the application of FAST testing system in the area of testing,evaluating,and predicting wool fabrics′ overfeeding sewing-shrinkage,The theory model was found between the ratio of fabric sewing-shrinkage,the ratio of fabrics′ bending modulus to stretching modulus(modulus ratio of bending and stretching),and fabric overfeeding capacity and other physical items.
为开发FAST客观测试仪在测试、评价、预测毛面料超喂缝制下缝缩率等有关方面的应用,建立了面料超喂缝纫时缝缩率与织物弯拉模量比(弯曲模量与拉伸弹性系数之比)、超喂量物理指标之间的理论方程,在分析面料弯拉模量比与FAST测试指标之间关系的基础上,推导了利用FAST测试弯拉模量比的计算方法。
4) flexure modulus
弯曲模量
1.
The results show that the changes of the flexure modulus can be divided into three stages in the fatigue experiment.
结果表明在疲劳过程中复合材料的弯曲模量有 3个变化阶段 :首先在疲劳加载初期 ,弯曲模量的下降速度及幅度都较大 ;其次在弯曲模量下降到原始弯曲模量的 85 % (13 3GPa)后 ,其变化方式没有明显的规律可循 ,有时甚至可能上升 ;最后复合材料发生疲劳断裂时 ,模量将发生突变 。
2.
According to the material structure of 3-D braided composites, a method of stiffness combination is proposed to predict material s flexure modulus.
根据三维四向编织复合材料的结构特点 ,提出了用刚度合成法来预测复合材料的弯曲模量 ,并对三维编织T30 0 /QY95 12复合材料的弯曲模量进行了预测 。
5) Equivalent material
等效材料
1.
By the finite element method,the linear and nonlinear deflections are calculated for the simple supported beams with original and equivalent materials properties.
利用整体—局部均质化法计算了钢筋混凝土材料的有效力学性质,并用经典Mori-Tanaka理论、蔡氏半经验半理论公式验证了该方法的可靠性,同时将钢筋混凝土材料等效成一种材料,用有限元法计算了原始材料与等效材料简支梁受集中荷载作用及对称弯曲作用的变形和应力。
6) Bending/?Bending modulus
弯曲/弯曲模量
补充资料：弯曲模量
分子式：
CAS号：
性质：又称挠曲模量。材料在弹性极限内抵抗弯曲变形的能力。用下式求得： 。式中，E为弯曲模量；L、b、d分别为试样的支撑跨度、宽度和厚度；m为载荷(P)-挠度(δ)曲线上直线段的斜率，单位为N/m2或Pa。
CAS号：
性质：又称挠曲模量。材料在弹性极限内抵抗弯曲变形的能力。用下式求得： 。式中，E为弯曲模量；L、b、d分别为试样的支撑跨度、宽度和厚度；m为载荷(P)-挠度(δ)曲线上直线段的斜率，单位为N/m2或Pa。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。