1) melamine formaldehyde moulding powder
三聚氰胺甲醛模塑粉
2) urea-melamine formaldehyde moulding powder
脲三聚氰胺甲醛模塑粉
3) asbestos filled melamine formaldehyde moulding powder
三聚氰胺甲醛石棉模塑粉
4) melamine formaldehyde moulding powder
三聚氰胺甲醛模塑料
5) melamine plastic
三聚氰胺(甲醛)塑料
6) melamine-formaldehyde
三聚氰胺-甲醛
1.
Microcapsules were prepared by the method of in-siu polymerization with melamine-formaldehyde as the outer membrane and a phase change materials as core,which melt point was 24℃.
以三聚氰胺-甲醛为壁材,十二醇为囊芯,采用原位聚合法制备了相变储热微胶囊。
2.
The microencapsulated phase change materials were prepared with in situ polymerization using dodecanol as the core, melamine-formaldehyde resin as the shell.
本文采用原位聚合法以十二醇为芯材,以三聚氰胺-甲醛树脂为壁材,制备微胶囊相变材料并对其进行性能表征。
补充资料：三聚氰胺甲醛模塑粉
分子式：
CAS号：
性质：由三聚氰胺甲醛树脂，加入漂白α-纤维素和润滑剂，浸渍后进行干燥，加入颜料，经球磨、过筛制得三聚氰胺甲醛模塑粉。其主要性能：流动性（拉西格），140～220mm；挥发物质≤4%；弯曲强度60～80MPa；冲击强度（缺口）1.5～2kJ/m2；热变形温度140～155℃；吸水性（冷水）≤35～50mg；收缩率0.20～1%；可抽取甲醛，3～30mg/L；水中24h后绝缘电阻≥104～105MΩ；电气强度≥5.0～10MV/m；介质损耗≤0.08～0.2MHz。
CAS号：
性质：由三聚氰胺甲醛树脂，加入漂白α-纤维素和润滑剂，浸渍后进行干燥，加入颜料，经球磨、过筛制得三聚氰胺甲醛模塑粉。其主要性能：流动性（拉西格），140～220mm；挥发物质≤4%；弯曲强度60～80MPa；冲击强度（缺口）1.5～2kJ/m2；热变形温度140～155℃；吸水性（冷水）≤35～50mg；收缩率0.20～1%；可抽取甲醛，3～30mg/L；水中24h后绝缘电阻≥104～105MΩ；电气强度≥5.0～10MV/m；介质损耗≤0.08～0.2MHz。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条