1) spun orientation
成形取向
2) orientation mapping
取向成像
1.
Analysis on behavior of dynamic recrystallization in magnesium alloy AZ31 by orientation mapping;
镁合金AZ31动态再结晶行为的取向成像分析
2.
The textural features during ferrite refinement by deformation enhanced transformation were analyzed by means of orientation mapping based on the EBSD technique in a Q235 low carbon steel.
利用背散射电子衍射取向成像技术分析了在热模拟单向压缩条件下Q235碳素钢形变强化相变时铁素体织构的类型。
3.
The texture evolution of ferrite during warm compression of Q235 low carbon steel was determined quantitatively by means of orientation mapping based on the EBSD technique.
利用背散射电子衍射取向成像技术定量分析了热模拟单向压缩条件下Q235碳素钢热变形时铁素体的织构形成规律。
3) achievement orientation
成就取向
1.
The achievement orientation of managers at different levels was studied by structural interview and behavioral event interview.
通过结构化访谈、行为事件访谈等方法 ,较为全面、深入地考察了企业各层次经理人员的成就取向及特点。
5) oriented nucleation
取向成核
6) orienting compression
取向成型
1.
As an important procedure for sintered and bonded magnets, orienting compression has direct influence on the property of the magnet.
取向成型是烧结和粘结磁体的一道重要工序,对最终磁体的性能有直接影响。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。