1) equivalent yield strength
当量屈服强度
1.
Based on the analysis and generalization of former research,the equivalent yield strength method suitable for hydro-forming of double-layered tubes was put forward,and the concrete approach to determine the equivalent yield strength was given.
文章在总结分析前人工作的基础上,提出了适用于双层管液压胀合的当量屈服强度法,给出了确定当量屈服强度的具体步骤。
2) yield
[英][ji:ld] [美][jild]
屈服;当量
3) yield strength increment
屈服强度增量
1.
Suggested is the mathematical relationship among yield strength increment ,precipitation phase volume precent fv and precipitation phase average radius dP in low alloy steel containing V.
导出了含V低合金钢的屈服强度增量△σp与桥出相倾粒平均直径dp、颗粒体积分数fv之间的数值关系式。
4) yield strength
屈服强度
1.
Effect of phosphorus on the yield strength of as-quenched GH761 alloy;
磷对GH761合金固溶水淬组织屈服强度的影响
2.
Study of influence factors of yield strength of oil and gas pipeline;
油气管道屈服强度影响因素的研究
3.
A modeling study of the yield strength of HRB335 hot rolled ribbed bar;
HRB335热轧带肋钢筋屈服强度模型研究
5) yield stress
屈服强度
1.
Based on the plain carbon steel with the chemical composition of 200MPa class steel the products of the yield stress of 400～500 MPa class and high-quality mechanical properties can be produced using the technology of chemistry tightly-tuning and controlled rolling - controlled cooling.
以屈服强度为 2 0 0MPa级的普碳钢为基本成分 ,采用成分微调与控轧控冷工艺相结合的技术路线 ,可将屈服强度提高到 4 0 0～ 5 0 0MPa,同时保证良好的综合性能。
2.
From the tests, a two-stage linear relation has been found between yield stress(σ_s) and strain rate(ε),σ_s=σ_0+klgε.
对４种金属材料进行了应变率为１０~（－４）—１０~３ｓ~（－１）的拉伸试验，结果表明，屈服强度随应变率的升高分两阶段线性升高。
6) yielding strength
屈服强度
1.
Yielding behavior of mismatched welded joint and prediction of its yielding strength;
非等强焊接接头屈服行为及屈服强度预测
2.
Mechanical properties of normalized and tempered 12Cr2Mo steel forgings,primarily yielding strength,were on the low side.
汽轮机用12Cr2Mo钢锻件经正火、回火后,其力学性能(主要是屈服强度)偏低,一次热处理后的合格率仅为50%,既造成该钢锻件大量热处理返修,又严重影响了生产周期。
补充资料：屈服
屈服
yield
屈服yield在外加应力下，材料开始发生不可逆的范性变形的现象。连续加载过程中，应力不增加或开始有所降低而材料如能继续变形，这种材料便具有明显的屈服现象，此时材料所承受的恒定、最大或最小应力分别称为材料的屈服点(飞)、上屈服点(隽u)或下屈服点(asL)。低碳钢及其他含有少量填隙元素的体心立方金属等都具有明显的屈服点:而不锈钢、面心立方金属及密集六角结构金属则无明显的屈服点。对于没有明显屈服现象的材料，很难准确测定它们发生塑性流变的起始点，工程上一般取永久变形值达0.2%时所对应的应力值为该材料的屈服强度，以a02表示。 屈服现象与材料中位错的形成、增殖及运动有关。体心立方金属中位错受到钉扎，不易运动，而且位错的运动速率对应力不敏感，可滑移位错的形成便标志着范性形变的开始，因而具有明显的屈服点。而面心立方金属中位错的运动速率对应力非常敏感，原生位错在低应力下就能运功，使面心立方金属不存在明显的屈服点。 (李宗全)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。