1) hydroxyl-terminated polybutadiene rubber
端羟基液体橡胶
1.
It is about the adhesion between hydroxyl-terminated polybutadiene rubber polyurethane elastomers and metal.
端羟基液体橡胶聚氨酯弹性体为柔性材料,丁羟聚氨酯弹性体硬度比丁腈羟聚氨酯弹性体小,前者的拉伸强度比后者稍大,伸长率也大;其作为粘合剂与金属粘接时,金属表面在分别经过酸化、磷化,喷砂、清洗,喷砂、清洗、涂偶联剂(KH-550)3种方法处理,其中金属表面进行喷砂、清洗、涂覆偶联剂时粘接性能最好。
2) hydroxyl-terminated polybutadiene/acrylonitrile rubber
端羟基液体丁腈橡胶
3) hydroxylated-terminated liquid polybutadine rubber
端羟基液体聚丁二烯橡胶
4) hydroxyl-terminated liquid polybutadiene rubber
端羟基聚丁二烯液体橡胶
1.
Preparation of organic montmorillonite/polyurethane/hydroxyl-terminated liquid polybutadiene rubber nanocomposites
有机蒙脱土/聚氨酯/端羟基聚丁二烯液体橡胶纳米复合材料的制备
5) Liquid Hydroxy-Terminated Butadiene-Acrylonitrile (HTBN)
端羟基液态丁腈橡胶(HTBN)
6) CTBN
液体端羧基丁腈橡胶
1.
CTBN MODIFIED BMI CONSTRUCTION ADHESIVE (Ⅱ)THE FORM AND PROPERTIES OF CTBN MODIFIED 1~#/DACPE;
液体端羧基丁腈橡胶改性双马来酰亚胺结构胶粘剂(Ⅱ)DACPE固化BMI体系胶粘剂的改性及形态结构
2.
Aminopolysiloxane and carboxy terminal butadiene-acrylonitrile (CTBN) were used to modify the epoxy resin system, and the heat-resistant epoxy adhesive cured at room temperature was prepared.
采用氨基硅油和液体端羧基丁腈橡胶(CTBN)对环氧树脂进行化学改性,制备出室温固化耐热环氧胶粘剂。
补充资料：液体丁腈橡胶
分子式：
CAS号：
性质：平均分子量小于1万的丁腈橡胶，呈液态。以过氧化氢异丙苯-乙二胺四乙酸钠-硫酸亚铁-雕白粉为引发剂，进行乳液聚合，聚合温度200℃，聚合时间4h，过氧化氢异丙苯分两次加入，胶液经真空脱气、凝聚、洗涤、干燥得到液体丁腈橡胶。其分子链中的丁二烯以反式1,4为主，两种链节呈无规分布。液体丁腈橡胶有良好的耐油性和黏着性，可与酚醛树脂、环氧树脂制成粘接力强、回弹性和耐油性好的胶黏剂。也可用作不抽出性专用增塑剂。
CAS号：
性质：平均分子量小于1万的丁腈橡胶，呈液态。以过氧化氢异丙苯-乙二胺四乙酸钠-硫酸亚铁-雕白粉为引发剂，进行乳液聚合，聚合温度200℃，聚合时间4h，过氧化氢异丙苯分两次加入，胶液经真空脱气、凝聚、洗涤、干燥得到液体丁腈橡胶。其分子链中的丁二烯以反式1,4为主，两种链节呈无规分布。液体丁腈橡胶有良好的耐油性和黏着性，可与酚醛树脂、环氧树脂制成粘接力强、回弹性和耐油性好的胶黏剂。也可用作不抽出性专用增塑剂。