2) acrylic modifed rosin type epoxy resin
丙烯酸改性环氧树脂
3) polyurethane modified epoxy-acrylate resin
聚氨酯改性环氧丙烯酸树脂
1.
The composition, characteristics, present situation, performances and preparation process of UV-curable waterborne polyurethane modified epoxy-acrylate resin and the energy-saving coatings therefrom are introduced.
介绍了光固化聚氨酯改性环氧丙烯酸树脂及其制备的节能涂料的组成、特点、现状、性能和制备方法。
4) Acryrylic acid modified bisphenol A epoxy resin
丙烯酸改性双酚A型环氧树脂
5) waterborne epoxy acrylate
水性环氧丙烯酸树脂
1.
Afterwards,waterborne epoxy acrylate(EB) was synthesized via the reaction of hydrophilic carboxy groups in maleic anhydride(MA) with the hydroxyl groups in EA.
在此基础上,通过顺丁烯二酸酐(MA)与EA上的羟基反应,在EA上引入了羧基亲水性基团,制备了水性环氧丙烯酸树脂(EB)。
6) epoxy acrylic resin
环氧丙烯酸树脂
1.
In this article the influences of catalyst、reaction temperature and inhibitors on synthetic reaction of epoxy acrylic resin, and effects of various active diluents, photoinitiators, promoters and substrates on the film properties were discussed, the finalized formulation of UV-curing coatings was given.
讨论了环氧丙烯酸树脂合成中的催化剂、反应温度和阻聚剂对反应的影响,以及不同活性稀释剂、光引发剂、促进剂和底材对涂膜性能的影响。
补充资料：尼龙改性环氧树脂
分子式：
CAS号：
性质：含环氧尼龙接枝共聚物结构并与F-44（环氧树脂）双氰胺预聚物共混制得的产物。用它制得的玻璃纤维增强塑料相对密度1.85～1.95。马丁耐热≥200℃。弯曲强度≥400MPa。压缩强度≥200MPa。冲击强度≥300kJ/m2。收缩率≤0.88%。吸水性≤0.05%。体积电阻率≥1013Ω·cm。由F-44双氰胺预聚物与E-51环氧树脂和尼龙6/66制得的接枝共聚物按比例混合制得。可用作尾翼片、穿甲弹弹托等。还可作增韧剂用于环氧、酚醛树脂，改善其柔韧性。
CAS号：
性质：含环氧尼龙接枝共聚物结构并与F-44（环氧树脂）双氰胺预聚物共混制得的产物。用它制得的玻璃纤维增强塑料相对密度1.85～1.95。马丁耐热≥200℃。弯曲强度≥400MPa。压缩强度≥200MPa。冲击强度≥300kJ/m2。收缩率≤0.88%。吸水性≤0.05%。体积电阻率≥1013Ω·cm。由F-44双氰胺预聚物与E-51环氧树脂和尼龙6/66制得的接枝共聚物按比例混合制得。可用作尾翼片、穿甲弹弹托等。还可作增韧剂用于环氧、酚醛树脂，改善其柔韧性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条