1) shear bond strength
粘接抗剪切强度
1.
In this study , we bonded resin orthodontic brackets to two kind of commonly - used prosthodontic materials: porcelain and light - cured composite resin with domestic adhesive, ordinary light - cured composite resin and BISCO ORTHO - ONE~? orthodontic Direct Bonding System respectively and then the shear bond strength of the re.
本实验通过使用不同的粘接剂粘接树脂托槽与经过不同方式表面处理的瓷和光固化复合树脂修复材料,对其粘接抗剪切强度,影响树脂托槽与修复材料直接粘接的因素以及去粘接后原修复面的完整性进行实验研究。
2.
In this study, we bonded metal orthodontic brackets to two kinds of commonly-used prosthodontic materials: porcelain and light-cured composite resin with domestic adhesive and ordinary light-cured composite resin respectively and then the shear bond strength of the metal brackets, the integrity of the prosthodontic surface after debonding and the microsco.
本研究使用国产的粘合剂和普通光固化复合树脂粘接金属托槽与瓷、光固化复合树脂两种常用的修复材料，并对其粘接抗剪切强度，去粘接后原修复面的完整性，表面处理后修复面的显微形态结构进行了实验研究。
2) Shear bond strength
抗剪切粘结强度
3) shear bond strength
剪切粘接强度
1.
5 mm/min was used to press samples,and values of shear bond strength(SBS)and types of interface failure were recorded and analyzed statistically.
5mm/min的生物力学测试机进行压缩剪切,记录各组剪切粘接强度值和界面断裂类型,并进行统计学分析。
4) bonding shear strength
抗剪粘接强度
1.
By adopting a new anchoring method, interfacial failure happened between CFRP sheets and concrete, the effective jointing length between Sika~ CarboDur~ CFRP sheets and concrete is about 200 mm, and the interfacial bonding shear strength reached 20～30 MPa.
试验结果表明,复合材料碳纤维板与混凝土的有效粘接长度约为200mm左右,碳纤维板与混凝土的界面抗剪粘接强度在20～30MPa之间。
5) strength of brazed joints in shear
接头抗剪切强度
6) Adhesion compression shearing strength
粘接压缩剪切强度
补充资料：剪切粘接强度
分子式：
CAS号：
性质：在平行于胶层的载荷作用下，胶接试样破坏时，单位胶接面所承受的剪切力，用MPa表示。根据载荷的方向有拉伸剪切粘接强度和压缩剪切粘接强度。
CAS号：
性质：在平行于胶层的载荷作用下，胶接试样破坏时，单位胶接面所承受的剪切力，用MPa表示。根据载荷的方向有拉伸剪切粘接强度和压缩剪切粘接强度。